Both Side Heat Sealable ,One Side Glossy Other Side Matte Film
TREATED, HEAT SEALABLE GLOSSY OPP LAYER
OPP CORE LAYER
UN-TREATED, HEAT SEALABLE MATTE OPP LAYER
Description
Both Side Heat Sealable ,One Side Glossy Other Side Matte Film
Features
Good matt dispersion
High haze & low gloss
Good printability
Good antistatic & slip
Application
Packaging & conversion
PROPERTIES
TEST METHOD (ASTM)
UNIT
TYPICAL VALUES
HHM-18
HHM-20
HHM-25
HHM-30
HHM-35
PHYSICAL
Thickness
ASTM D 374
MICRON
18
20
25
30
35
Grammage
NTM
gm/m²
15.66
17.4
21.8
26.1
30.45
Yield
NTM
m²/kg
63.8
57.5
46
38.3
32.8
Thickness variation
%(±)
3
SURFACE
Treatment Level (min)
ASTM D 2578
dyne/cm
38
OPTICAL
Haze
ASTM D 1003
%
70-75
Gloss
Glossy
Matte
ASTM D 2457
-
-
50-52
11-13
MECHANICAL
Coefficient Of Friction
ASTM D 1894
Static
Kinetic
0.40-0.45
0.30-0.35
Tensile Strength
MD
TD
ASTM D 882
kg/cm²
1100-1300
2200-2700
Modulus
MD
TD
ASTM D 882
kg/cm²
14000-17000
24000-28000
Elongation
MD
TD
ASTM D 882
%
%
140-180
40-80
THERMAL
Shrinkage at 120°C/5min
MD
TD
ASTM D 1204
%
%
2.0-4.0
1.0-3.0
Seal Initiation Temperature (Max)
NTM
°C
115-118
Sealing Strength (min) at 120ºC/2Bar
NTM
gms/25mm
250-300
DISCLAIMER
The values given in this technical datasheet are typical performance data and are believed to be accurate .These are given in good faith but it is for the customer to satisfy of the suitability for its
own particular purpose. NAHAR POLY FILMS LTD. Suggests to the customer to confirm these values and product compatibility prior to their use and the company offers neither guarantee nor
accept any responsibility for the fitness of the product for any other use.
NTM: NAHAR TEST METHOD, MD : MACHINE DIRECTION ,TD : TRANSVERSE DIRECTION